Rustproofed Thermal Spray Coatings With ASTM-C633 NEN-EU 5 Standard
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xStructure | Piston Cylinder | Power | Hydraulic |
---|---|---|---|
Body Material | Steel | Product Name | Thermal Spray Coatings |
Typical Coating Composition | Inc625-Cr2O3TiO2 | Bond Strength | > 40MPa |
Macro Hardness | 65 HRC | ||
Highlight | metal spray coatings,ceramic spray coatings,65 HRC Thermal Spray Coatings |
Rustproofed Thermal Spray Coatings With ASTM-C633 NEN-EU 5 Standard
Description:
Anti-corrosion and salt spray test > 4000hrs
Macro hardness 65 HRC
Maximum temperature 540˚C
Bond strength > 40MPa
Standard: ASTM-C633 ,NEN-EU 5,NEN-ISO 4287,NEN-ISO 4287,ASTM D2794-93
NEN-ISO 4287,DIN50021-155,TNOCA02.8043
HYDROX AP20 Coating Technical Specifications
List of items | HYDROX AP20 | Standard |
Typical coating composition | Inc625-Cr2O3TiO2 |
|
Coating thickness | Bottom ( Inc625) ≥150um |
|
| Surface layer ( Cr2O3TiO2) ≥200um |
|
Bond strength | > 40MPa | ASTM-C633 |
Maximum temperature | 540˚C |
|
Porosity | < 2% |
|
Macro hardness | 65 HRC |
|
Micro hardness | > 1000HV200 | NEN-EU 5 |
Surface Finish (Ra) | 0.15um-0.4um | NEN-ISO 4287 |
Surface Finish (Rz) | < 4.5um | NEN-ISO 4287 |
Shock Value | > 2J | ASTM D2794-93 |
RPK Material contact area | > 80%,Depth 1,0um | NEN-ISO 4287 |
Anti-corrosion and salt spray test | > 4000hrs | DIN50021-155 |
ECP(Drying) | < -350mV |
|
ECP(Semi-dry) | < -350mV | TNOCA02.8043 |
ECP(Wet) | < -350mV |
|
APPLICATIONS OF THERMAL SPRAY COATINGS
To apple ceramic coating on the equipment surface can have many benefits, such as high hardness, high temperature resistance, corrosion resistance, salt fog resistance etc. The effect is much better than common electroplating. It works well in ocean industry, food machinery, water conservancy and hydropower, aerospace and other industries.